600°C High-Temperature Organosilicone Coating
Group Please provide the Chinese content you would like translated into American English. ByOrganosiliconResin, active rust-proof pigments, penetrants, hardeners, additives, etc.。
Sex Available This productHigh-temperature resistance with excellent weather and corrosion resistance. Post-high temperature treatment, the organic silicon and inorganic silicate materials bond together, thereby protecting the base material. This product improves the poor corrosion resistance of previous organic silicon coatings under normal and high temperatures, as well as during water wash rinsing and alternating cold and hot conditions.
Please provide the Chinese content to be translated. Path Commonly used for temperatures ranging600Surfaces of materials below 0°C serve decorative, protective, and anti-corrosion and anti-rust purposes. Such as in fire bowls, barbecue grills, car exhaust pipes, and fireplaces, etc.
Product Specifications
Temperature Resistance Range | Film Color | Coating Type | Blend Ratio |
600℃ | Gray | Primer | Single-component, two-component |
600℃ | Black, white, gray, aluminum powder, etc. | Face paint | One-component, two-component |
Technical Specifications
Project | Index |
Color | Undercoat: Gray Surfaces Paint: Black, White, Grey, Aluminum Powder, etc. |
Gloss | Undercoat: Matte Flat or Semi-Gloss Paint |
Viscosity | 25-60s（25±1°F, coated-4） |
Drying Time （23±2℃） | Primer: Surface dry≤1h, Action ≤24h Surface Paint: Surface Dry≤2h, Doing Business ≤24h |
Flexibility | ≤2mm |
Adhesion | ≤2Grade |
Impact resistance | ≥40kg·cm |
Thermal resistance600℃，2h） | Non-bubbling and non-cracking |
Shelf Life | 25°C, Store away from light3-6month |
Construction Method
1. Base Material Processing
Before painting, the substrate surface should be cleaned of oil, rust, foreign matter, etc. Sandblasting toSa2.5 grade, remove remaining paint, rust, and oxidation scales.
2. Mixed (for two-component paints)
Priced by weight ratio (as indicated on the product packaging)
When mixing, slowly add the hardener while continuously stirring the main agent to ensure thorough and even mixing.
Mixed paint agingAfter 20 minutes, filter through a 60-80 mesh sieve and pour into another container for later use.
Shelf life of mixed paint3 hours, please use according to the construction progress.
3. Baking (suitable for one-component paint)
Product Name | Baking Temperature | Insulation Time |
High-Temperature Organic Silicon Coating with Resistance up to 600℃ | 220℃ | 30min |
280℃ | 20min |
4. Construction Conditions
Spraying operations should be carried out as soon as possible after the substrate treatment, generally not exceeding8 hours. The surface temperature of the substrate and the ambient temperature should generally not be below 10°C, with the surface temperature at least 3°C above the dew point, and the relative humidity of the air should not exceed 85%.
5. Painting Methods
This paint can be applied using brush painting, airless spraying, and air-assisted spraying methods.
6. Dilute
In most cases, paint requires a compatible thinner to adjust viscosity and clean tools.
7. Coating Interval
One-component paint is ready for subsequent coating after drying. For two-component paint, the recommended curing interval is as follows:
Substrate Temperature | 5℃ | 20℃ | 30℃ |
Short | 48h | 24h | 12h |
Long | Unrestricted | ||