Description

It comes in both graphite and non-graphite varieties. Particle sizes include: 1.0~1.5mm, 1.5~2.0mm, 2.0~3.0mm. It melts and rapidly expands within the injection sleeve and at the tip, forming an excellent lubricating film inside the sleeve due to its capillary effect. It's easy to use and does not require the traditional spray systems with drip-painting pumps used for oil-based or water-based products.

Appearance: White, yellow, transparent (without graphite), granular.

Applicable Range: Pressure Fit Bushings with diameter ranging from 50-120mm; Black Granules: Containing Graphite, spherical in shape.
Density at 20℃: 0.5-0.7 cm³.
Application Range: Injection sleeves with diameters ranging from 50 to 160mm.

[Usage Instructions]

Add granules to the casting chamber using a particle emitter.
Usage based on different punch diameters
60mm 0.4-0.5g
80mm 0.6-0.8g
100mm 1.0-1.3g
140mm 1.7-2.5g
150mm 2.2-4.0g
The determination of usage depends on the casting weight and requires empirical testing.

【Advantages】

No pollution produced by general oil-based lubricants.
2. Reduce the occurrence rate of casting porosity.
3. Extends the service life of the plunger tube and reduces the adverse effects caused by friction.
4. The lifespan of a die-casting punch used in factories is generally doubled compared to using pure oil lubrication.
5. Increase jet speed.
6. Complete consumption of particles during casting, free of lubricant contamination.
7. The die-castings have no oil stains on the surface, presenting a clean and shiny finish.
8. When the gating, runner, and riser are recycled for use, they are free of oil stains, smoke, and air pollution.
9. No wastewater treatment required, no water cooling system or cleaning nozzle needed.
10. Highly economical usage, saving on expenses.
11. Enhance process safety.