Glass Flake Mortar (Medium Temperature)
Resin Type: Epoxy Acrylic Vinyl Ester Resin
Features: Excellent chemical resistance, solvent resistance, and impermeability
Main applications: lining for flue gas desulfurization units, various chemical equipment, etc.
Liquid: ≤120℃; Gas: ≤130℃; Appearance: White, semi-transparent, pale green, pale blue.
Achieve a coating thickness of 2mm in two to three coats.
Coating Methods: Blade and Trowel Application
Specific Gravity: 1.4-1.8
Coating Amount: Practical Value: 3.8 kg/m²
Construction Ratio (wt/%): Main Agent : Initiator : Accelerator
100：1～1.5：0.5～1
4 hours to 30 days interval
Operating conditions: Environmental temperature: 5℃-30℃
Relative Humidity: Below 85%
Packaging Agent: Iron Drum (20L)
Initiator and accelerator: plastic containers (5L or 10L)
Storage Method: Store in a cool, dry place, avoid direct sunlight.
Shelf life: 3 months at 20°C, 6 months at 15°C
Glass Flake Mortar (High Temperature)
Phenolic Epoxy Vinyl Ester Resin
Excellent chemical resistance, solvent resistance, and permeation resistance.
Primary applications include lining for flue gas desulfurization units, various chemical equipment, etc.
Liquid: ≤100℃; Gaseous: ≤200℃
Coating thickness: 2mm / completed in two to three coats
Coating Methods: Trowel and spatula application
Physical Appearance: White, semi-transparent/light green, light blue.
Specific Gravity: 1.4-1.8
Coating Amount: Practical Value: 3.5 kg/m²
Construction Ratio (wt/%): Main Agent : Initiator : Accelerator
100：1～1.5：0.5～1
Interval: 4 hours to 30 days
Operating conditions: environmental temperature: 5℃-30℃
Relative Humidity: Below 85%
Packaging Agent: Iron Drum (20L)
Initiator and Accelerator: Plastic Containers (5L or 10L)
Storage Method Store in a cool, dry place, avoid direct sunlight
Shelf life is three months at 20°C, six months at 15°C.
Product Description
1. Glass flake mortar features an anti-penetrating barrier with low permeability to corrosive gases.
2. Excellent resistance to water, acids, alkalis, some solvents, and other special chemical media.
3. Glass flake mortar has minimal shrinkage upon hardening, strong adhesion to various substrates, and is easy to repair locally.
4. High tensile glass flake mortar with excellent mechanical properties, adaptable to rapid temperature changes.
5. Glass flake adhesive mud cross-links and solidifies, featuring high surface hardness and excellent wear and corrosion resistance.
6. Long-term service temperature for glass flake mortar: wet state 100/180°C, dry state 120/200°C.
7. Compared to glass fiber reinforced plastic, the outstanding advantage of glass flake mortar is its excellent impermeability, with an impermeability rate approximately equal to that of glass fiber reinforced plastic.