Glass Flake Mortar (Medium Temperature)
Resin Type: Epoxy Acrylic Vinyl ester Resin
Features: Excellent chemical resistance, solvent resistance, and permeation resistance
Main applications: lining for flue gas desulfurization units, various chemical equipment, etc.
Liquid at use temperature: ≤120℃; Gaseous at use temperature: ≤130℃; Appearance: White, semi-transparent, pale green, pale blue.
Achieve a coating thickness of 2mm in two to three coats.
Coating Methods: Blade and Trowel Application
Specific Gravity: 1.4-1.8
Coating Amount: Practical Value: 3.8 kg/m²
Construction Ratio (wt/%): Main Agent : Initiator : Accelerator
100：1～1.5：0.5～1
Interval: 4 hours to 30 days
Operating Conditions: Environmental Temperature: 5℃-30℃
Relative Humidity: Below 85%
Packaging Agent: Iron Drum (20L)
Initiators and Accelerators: Plastic Containers (5L or 10L)
Storage Instructions: Store in a cool, dry place, away from direct sunlight.
Shelf life: three months at 20°C, six months at 15°C.
Glass Flake Mortar (High Temperature)
Phenolic epoxy vinyl ester resin
Excellent chemical resistance, solvent resistance, and impermeability.
Main applications: linings for flue gas desulfurization units, various chemical equipment, etc.
Liquid Temperature Usage: ≤100℃; Gaseous Temperature Usage: ≤200℃
Coating thickness: 2mm / completed in two to three coats
Coating Methods: Spread with a spatula or trowel
Property Color: White, semi-transparent/light green, light blue.
Weight Ratio: 1.4-1.8
Coating Amount: Practical Value: 3.5 kg/m²
Construction Ratio (wt/%): Main Agent : Initiator : Promoter
100：1～1.5：0.5～1
4 hours to 30 days interval
Operating conditions: ambient temperature: 5℃-30℃
Relative Humidity: Below 85%
Packaging Agent: Iron Drum (20L)
Initiators and accelerators: Plastic containers (5L or 10L)
Storage Method Store in a cool, dry place, avoid direct sunlight
Shelf life is three months at 20°C and six months at 15°C.
Product Description
1. Glass flake mortar features an anti-permeation barrier with low permeability to corrosive gases.
2. Excellent resistance to water, acids, alkalis, certain solvents, and other special chemical media.
3. Glass flake mortar has minimal shrinkage upon curing, strong adhesion to various substrates, and is easy to patch locally.
4. High-tensile glass flake mortar with excellent mechanical properties, suitable for rapid temperature changes.
5. Glass flake mortar cross-links and solidifies, featuring high surface hardness and excellent wear and corrosion resistance.
6. Glass flake mortar serviceable temperature: Wet state 100/180°C, dry state 120/200°C.
7. Compared to glass fiber reinforced plastic, the outstanding advantage of glass flake mortar is its excellent anti-seepage performance, with an anti-seepage rate approximately equal to that of glass fiber reinforced plastic.