316Ti stainless steel plate, in accordance with the national standard, is equivalent to 1Cr18Ni12Mo2Ti stainless steel plate in China's nomenclature. The 316Ti stainless steel plate is enhanced with Ti in the SUS316 steel to improve its intergranular corrosion resistance.
Equipment for resisting sulfuric acid, phosphoric acid, acetic acid, and vinegar.
Physical Properties





Chemical Composition
C：≤0.08
Si≤1.00
Mn≤2.00
P≤0.035
S≤0.030
Ni 11.00~14.00
Cr 16.00~19.00
Mo 1.80~2.50
Ti≥0.2~0.70
GB/T1220-1992 specifies this, commonly referred to as Mo2Ti or 316Ti.




Mechanical properties
YS（Mpa） ≥205
TS（Mpa） ≥520
EL（%） 　≥40
Approx. 200° Hv
Thickness: Cold Rolled 2B Sheet (0.09—6.0mm)
Hot-rolled industrial plates (3-50mm), medium and heavy plates, chemical plates, and high-temperature plates.
Width: 5mm to 850mm steel strip
1000, 1219, 1250, 1500, 1800, 2000mm coil, flat plate
Surface: 2B Smooth, Industrial, BA (6k) Mirror, 8K Mirror, 9K Mirror, Brushed, Matte.
Origin: Domestic, Imported (Sweden, Japan, Finland, South Korea, South Africa, Taiwan)



Key Attributes

These properties refer to the product's characteristics, which are similar but not identical to those of other products, such as plates and forgings, as specified in their respective standards. Lower *preheat and postheat temperatures reduce the incidence of weld defects, cracking, and simplify welding. The reduced hardness in the heat-affected zone *minimizes degradation in mold performance.