UBE 1030BProduced by Ube Industries in Japan, this is a PA6 resin of extrusion grade with high viscosity. Our company has been supplying PA6 plastic raw materials with excellent high-pressure heating resistance, good wear resistance, excellent oil resistance, low odor transferability, and tube-grade characteristics for various applications.NylonExcellent weather resistance, inert to biological erosion, with good antibacterial and antifungal properties. NylonExcellent electrical insulation properties; high volume resistance of nylon, high breakdown voltage; can be used as a power frequency insulating material in dry conditions, still retaining good electrical insulation properties even in high humidity environments. NylonParts are lightweight, easy to dye, and moldable. Due to their lower melt viscosity, they flow quickly. They are easy to fill the mold, and after molding, have a high freezing point, allowing for rapid solidification, thus shortening the molding cycle.
| Physical Properties | Rated value | Unit System | Testing Method |
Density | 1.14 | g/cm³ | ISO 1183 |
Shrinkage rate | Internal Method | ||
Lateral flow | 1.2 | % | |
Traffic | 1.2 | % | |
Absorption rate (Balance, 23°C, 50% RH) | 2.5 | % | Internal Method |
| Mechanical Properties | Rated Value | Unit System | Testing Method |
Tensile Modulus | 2800 | MPa | ISO 527-2 |
Tensile Stress Submit | 80.0 | MPa | ISO 527-2 |
Tensile strain (Broken) | > 50 | % | ISO 527-2 |
Bending Modulus | 2700 | MPa | ISO 178 |
Bend Strength | 110 | MPa | ISO 178 |
| Impact Resistance | Rated Value | Unit System | Testing Method |
Simply Supported Beam Notch Impact Strength | 5.0 | kJ/m² | ISO 179 |
| Thermal performance | Rated Value | Unit System | Testing Method |
Hot deformation temperature | |||
0.45 MPa, Annealed | 145 | °C | ISO 75-2/B |
1.8 MPa, annealed | 60.0 | °C | ISO 75-2/A |
Linear Coefficient of Thermal Expansion - Flow | 0.000080 | cm/cm/°C | ISO 11359-2 |