The Xuchang Infrared Technology Research Institute Co., Ltd. is located at Yongxing East Road, High-tech Development Zone of Xuchang, Henan (Zhongyuan Electrical Valley), and was previously the Xuchang Infrared Technology Research Institute. It is one of the influential infrared heating research institutions in China.
I am from1979Year10Since its establishment last month, adhering to“Highlight strengths, stringent quality control, enhanced service, strive for excellencel”The guiding philosophy. With its robust technical strength, a high-quality team of employees, and a spirit of innovation, Xuchang Infrared Institute has developed and produced a series of national-level products.jInfrared products for pre-watering. Main products include: series of infrared radiation (absorption) coatings, infrared heating elements, infrared radiation heating modules (plates), infrared radiation heating ovens (boxes), rapid infrared radiation heaters, seriesgEnd infrared heating experimental equipment, series of infrared heating controllers, etc.
This paint is a high-performance infrared-resistant high-temperature coating, with a film that exhibits excellent sealing properties after curing. The product is capable of...(Visual color)Durable 250 - 800 ℃High temperature.
Suitable for all high-temperature environments, it protects against erosion by high-temperature corrosive media. Such as engine casings, chimneys, exhaust pipes, heat exchangers, etc. The coating surface appears smooth..Impact resistance in kg/centimeters50.Adhesion(Circle marking method)Grade20.Drying Time:Drying table(h)< 0.5.
(1):The surface of the object must be cleaned of dust, oil, weld slag, rust, and old paint film prior to painting. , Steel Sheet Surface requirements for sandblasting and shot blasting to Sa2.5Grade Local surface repairs require sanding to St3 No water is permitted during construction.
(2):This material is ready for application after single-component mixing. The mixing ratio for two-component coatings is. The application mixing ratio method for two-component coatings is.:Open the A component wide open, add the B component to the A component, and stir thoroughly. Uniform. Ready for painting.
(3):Paint too thick, can be thinned with diluent. Unused materials must be sealed and stored.
(4):Overcast or relative humidity above 75% When necessary, construction should cease.
(5):Products should be stored in a cool and dry place.,Prevent direct sunlight exposure , Isolate ignition sources , Keep away from heat sources.
(6):Shelf life is 12 months. , After expiration, all technical indicators should be inspected. , As per target requirements , Continue to use.
Infrared high-temperature paint, also known as infrared high-temperature lacquer, infrared heat-resistant paint, and infrared heat-resistant lacquer, is divided into organic silicon and inorganic silicon high-temperature paint series.,As the name implies, it is paint that can withstand high-temperature oxidation and corrosion from other mediums.
Infrared silicone high-temperature paint offers protective features including corrosion resistance, waterproofing, oil resistance, chemical resistance, light resistance, and temperature resistance. Exposure to the atmosphere can cause items to be eroded by oxygen and moisture, leading to metal rust, wood decay, and concrete weathering. Applying paint to the surface forms a protective layer that can prevent or delay these destructive processes, thereby extending the service life of various materials.
Infrared silicone high-temperature paint Paint Painting Application Reference:High-temperature silicone paint Ensure the base material is cleaned thoroughly before applying paint, strictly prevent moisture, dust, and other impurities to ensure the adhesion of the paint film. Infrared high-temperature silicone paint Paint and coating films reach the specified thickness,Regular temperature and humidity control required.2Available for use in 3 days. High-temperature resistant infrared silicone paint Painting infrared coating paint during application, as required by the construction needs(As brushing, spraying)Available for dilution with solvent for high-temperature infrared silicone paint Increase ventilation during paint and coating application to prevent poisoning..Construction site strictly prohibit open flames to prevent fires. High-temperature resistant infrared silicone paint Paint and coatings have an effective shelf life of1Year, products beyond storage period may be inspected according to this standard.,Compliant and still usable
Widely applied for high-temperature corrosion protection on the inner and outer walls of blast furnaces, hot blast stoves, chimneys, flues, drying chambers, exhaust pipes, high-temperature hot gas pipes, heating furnaces, heat exchangers, and other non-metallic and metallic surfaces.
Based on the temperature resistance range,Generally, the price increases with every additional hundred degrees.60Yuan/pound,If there are any additional requirements for the coating film, the price will be correspondingly higher.
Infrared high-temperature paint technical specifications Film appearance:The paint film is smooth and even, black meets the standard sample..Drying Time:Standard thickness, single-coated.25℃Drying film≤2Hour, hard work≤24Hour pencil hardness:≥HEnclosed Please provide the Chinese content you would like translated into American English. Power:≤2(Circular marking method, level)Impact Strength:50k·cmBend Test:≤1mmSalt-resistant(3%Saltwater25℃，30Sky):Non-bubbling, non-rusting, non-flaking
Acid resistance(20%Sulfuric Acid25℃，30Sky):Non-bubbling, non-rusting, non-flaking
Alkali-resistant water(10%NaOH，25℃，30Sky):Non-bubbling, non-rusting, non-peeling
Infrared High-Temperature Paint Basic Parameters Matching Please provide the Chinese content you would like translated into American English.: Paint materials:Curing agent = 4:1(Weight Ratio)
Construction Time Limit:8h，(25℃)Theoretical Usage:250~350g/m2.Fully cured:7Sky
Excellent stability, can withstand350~400℃Unfading600℃Turns yellowish-brown, to1200---,1300℃Changes to an irreversible black-brown color.
The heat resistance of the chemical in white paint is250~300℃Applicable to250℃Long-term heat resistance.
In black pigments, carbon black is suitable for250℃Long-term heat resistance, if the temperature is higher than300℃Colors may fade. Graphite powder and manganese dioxide are suitable for300℃Above, long-lasting heat resistance.
Iron oxide red and cadmium red in red pigments are suitable for250℃Long-term heat resistance.
Yellow pigment with resistance200℃Extended periods of high temperature.
In blue pigment applications200℃Below heat-resistant;Indigo can withstand200℃Long-term high temperatures250℃Above will fade;Cobalt blue is suitable for500℃Long-term heat resistance.
Trichromic Chromium and Cobalt Green pigments in green paints are suitable for250℃Long-lasting heat resistance.
Melting point approximately600℃Therefore, it is commonly prepared to be durable.500~600℃Infrared high-temperature paint.xThe melting point of the powder is approximately420℃，at900℃Vaporized, thus often prepared400℃High-temperature resistant paint.
(1) Pre-treatment:Base Material SurfacebPlease use shot blasting treatment.Sa2.5Grade;
(2) Wipe the workpiece surface with a solvent.;
(3) Adjust paint viscosity with a配套diluent; use the diluent as the diluent, approximately in the amount of:Airless Spray--About5%(By paint weight);Air Spray--About15-20%(By paint weight);Brush coating--About10-15%(By weight of paint);
(4) Construction Method:Airless Spray, Air Spray, or Brushing. Note::Substrate temperature during constructionbMust exceed the dew point3℃However, not exceeding60℃;
(5) Paint curing:After application, the coating is allowed to cure naturally at room temperature before use or drying at room temperature.0.5-1.0hour, then place180-200℃Bake in the oven0. 5Remove and cool for later use.
Density--About1.08g/cm3;
Dry Film Thickness(A dish)25um;Wet Film Thickness56 um;
Flash Point-27℃;
Coating Quantity--120 g/m2;
Coating interval time:8-24Hour/25℃Below,4-8Hour/25℃Above.
Paint shelf life:18Months. Beyond this period, still usable upon passing inspection.
Self-drying infrared silicone high-temperature paint composed of modified organic silicon resin, heat-resistant pigments, additives, and solvents.
Film color A variety of colors,Meets the standard sample and its color variation range, with a smooth and even film coating..
Solid Content 65%.Finenessum≤ 20.Specific Gravity 1.36.Drying Time≯ Table dry10 Pragmatic24.Coating Film Thickness Dry Film:20-40umPlease provide the Chinese content to be translated. Wet Film:80-150um/Coverage rate Theoretical Value:6.5square meters/Ascend/40um
Actual Value:Factors related to surface treatment, external environment, construction methods, etc.
Water resistance24h Non-bubbling,wrinkle-free,No shedding,Permitted for film whitening,24hRestore
(1)Surface to be coatedbMust be cleaned thoroughly,Dry, neutral, oil-free(2)Tools used during constructionbEnsure dry and clean(3)bUse the recommended thinner.,Do not mix with coatings of other types. Spray viscosity is adjusted according to the job site.(4)Construction and drying time,Relative humidity not exceeding75%Otherwise, it may cause the paint film to bubble.(5)The construction site has good ventilation conditions and necessary protective gear is worn.XWGTModel High Temperature Infrared Radiation Coating88Named as a recommended energy-saving project in Henan Province annually, and awarded the Third Prize in Science and Technology Progress in Xuchang City.2002In the year, we developed and produced nano low-temperature infrared radiation coatings.
Xuchang Infrared Institute will continue to focus on the research and development of infrared radiation heating technology to enhance safety.qEfficiency, reliability, and system lifespan, providing for you,zPure infrared heating technology solutions.