详情描述
High-temperature resistant silicone coating, withstands up to 200°C
Composition ByOrganosiliconResin, active rustproof pigments, penetrants, hardeners, additives, etc.。
Performance This productBoasts high-temperature resistance, as well as excellent weathering and corrosion resistance. After high-temperature treatment, the organic silicon and inorganic silicate are bonded together, thereby protecting the base material. This product improves the poor corrosion resistance of previous organic silicon coatings under normal temperature, high temperature, and water washing scrubbing with alternating cold and hot conditions.
Usage Commonly used for temperatures ranging200Steel and cement surfaces below °C serve decorative, protective, and anti-corrosion and rust functions.
Product Specifications
Temperature Resistance Range | Film color | Coating Type | Mixed Ratio |
200℃ | Iron red, gray | Primer | Single-component, two-component |
200℃ | Black, white, gray, red, yellow, blue, green, aluminum powder, etc. | Surfaces Paint | Single-component, two-component |
Technical Specifications
Project | Benchmark |
Color | Base Coat: Gray, Iron Red Surfaces Paint: Black, white, gray, red, yellow, blue, green, metallic silver, etc. |
Luster | Undercoat: Matte Flat or Semi-Gloss Paint |
Viscosity | 25-60s（25±1°C, coated-4） |
Drying Time （23±2℃） | Primer: Surface dry≤1h, Doer ≤24h Topcoat: Surface Dry≤2h, Action ≤24h |
Flexibility | ≤2mm |
Adhesion | ≤2Grade |
Impact resistance | ≥40kg·cm |
Thermal resistance200，2h） | Non-bubbling and non-cracking |
Shelf Life | 25°C, Store away from light12month |
Construction Method
1. Base Material Processing
Prior to painting, the substrate surface should be cleaned of oil, rust, foreign matter, etc. Sandblasting toSa2 grade, remove residual paint, rust, and oxide scale.
2. Mixed (for two-component paints)
By weight ratio (as indicated on product packaging)
While mixing, slowly add the hardener to the main agent, ensuring it is thoroughly mixed.
Pre-mixed Paint MaturationAfter 20 minutes, filter through a 60-80 mesh sieve and pour into another container for later use.
Shelf life of mixed paint3 hours, please use according to the progress of construction.
3. Baking (suitable for one-component paint)
Product Name | Baking Temperature | Insulation duration |
200°C High-Temperature Organic Silicon Coating | 140℃ | 20min |
4. Construction Conditions
Spraying operations should be carried out as soon as possible after the substrate treatment, generally not exceeding8 hours. The surface temperature of the base material and the ambient temperature should generally not be below 10°C, with the surface temperature at least 3°C higher than the dew point, and the relative air humidity should not exceed 85%.
5. Painting Methods
This paint can be applied using brush coating, airless spraying, and air-assisted spraying methods.
6. Dilute
Generally, paints require a compatible thinner to adjust viscosity and clean tools.
7. Coating Spacing
One-component paint is ready for subsequent coating after drying. For two-component paint, it is recommended to follow the coating interval as follows:
Substrate Temperature | 5℃ | 20℃ | 30℃ |
Short | 48h | 24h | 12h |
Long | Unlimited | ||