详情描述
High-temperature resistant silicone coating, up to 300℃
Group Please provide the Chinese content you would like translated into American English. ByOrganosiliconResin, active anti-rust pigments, penetrants, hardeners, and additives, etc.。
Please provide the Chinese content to be translated. Available This productBoasts high-temperature resistance, excellent weathering and corrosion resistance. After high-temperature treatment, the organic silicon and inorganic silicate materials bond together, thereby protecting the base material. This product improves the poor corrosion resistance of previous organic silicon coatings under normal and high temperatures, as well as during water washing and cold-hot alternation.
Please provide the Chinese content you would like translated into American English. Path Commonly used for temperatures ranging300Steel and cement surfaces below ℃ serve decorative, protective, and anti-corrosion and rust functions.
Product Specifications
Temperature Range | Film Color | Coating Type | Mixed Ratio |
300℃ | Iron red, gray | Primer | Single-component, two-component |
300℃ | Black, white, gray, red, yellow, blue, green, aluminum powder, etc. | Surfaces Paint | One-component, two-component |
Technical Specifications
Project | Index |
Color | Primer: Gray, Iron Red Surfaces Paint: Black, White, Grey, Red, Yellow, Blue, Green, Silver Powder, etc. |
Gloss | Undercoat: Matte Flat or Semi-Gloss Finish |
Viscosity | 25-60s（25±1°C, coated-4） |
Drying Time （23±2℃） | Undercoat: Surface Dry≤1h, Action ≤24h Surface Paint: Varnish≤2h, Doer ≤24h |
Flexibility | ≤2mm |
Adhesion | ≤2Grade |
Impact resistance | ≥40kg·cm |
Thermal resistance300℃，2h） | Non-bubble and non-crack |
Shelf Life | 25°C, Store away from light12month |
Construction Method
1. Material Treatment
Before painting, the substrate surface should be cleaned of oil, rust, foreign matter, etc. Sandblasting toSa2 grade, remove residual paint, rust, and oxide scales.
2. Mixed (for two-component paint)
Weight-proportional as indicated on product packaging
While mixing, slowly add the hardener to the main agent, stirring continuously to ensure thorough mixing.
Pre-mixed Paint MaturationAfter 20 minutes, filter through a 60-80 mesh sieve, and pour the mixture into another container for later use.
Shelf life of mixed paint3 hours, please use according to the construction progress.
3. Baking (suitable for single-component paint)
Product Name | Baking Temperature | Insulation Duration |
High-temperature resistant silicone coating, withstanding up to 300℃ | 200℃ | 20min |
4. Construction Conditions
Spraying operations should be conducted as soon as possible after the substrate treatment, generally not exceeding8 hours. The substrate surface temperature and ambient temperature should generally not be below 10°C, with the surface temperature at least 3°C above the dew point, and the relative air humidity should not exceed 85%.
5. Coating Methods
This paint can be applied using brush painting, airless spraying, and air-assisted spraying methods.
6. Dilute
Generally, paint requires a compatible thinner to adjust viscosity and clean tools.
7. Coating Spacing
One-component paint can be coated after drying. For two-component paint, it is recommended to follow the coating interval time as follows:
Substrate Temperature | 5℃ | 20℃ | 30℃ |
Short | 48h | 24h | 12h |
Long | Unrestricted | ||