Features:

Good adhesion — durable and not easily peeled off.
2. Fine grain — Suitable for castings with surface fine textures, ensuring a beautiful appearance.
3. Excellent release properties — easy to demold without sticking.
4. Non-corrosive – Extends the life of iron molds.

Usage Instructions:

1. First, clean the iron mold surface thoroughly (no oil, release agent residue, or debris), as oil will reduce the adhesion of the release agent, especially for new molds. Pay attention to slight roughness and make sure the surface is easy to adhere to.
2. Heat the iron mold to 80-200°C.
3. Before diluting HS 865, please first mix it thoroughly. Then, dilute it with water at a ratio of 1:1 to 1:5 and ensure it is well mixed.
4. During spraying, use a fine-nozzle spray gun to apply a misty, even coating. Spray once on the mold surface, let it dry, then spray once more. Typically, 2-3 coats are sufficient before casting. Regarding the sprue, runner, and mold filling end, consider increasing the release agent spray thickness for better insulation. To reduce insulation or achieve a finer surface, reduce the spray thickness.
5. After the release agent is sprayed, reheat the mold to the casting mold temperature, and then proceed with the production.
6. When removing parts (such as corners, holes, etc.), there is a risk of pulling and scratching the casting, making it difficult to remove the mold effectively. To achieve this, apply a small amount of HS-L303 (aluminum lubricating release oil) to the mold coating surface corresponding to the casting's pull and scrape, for better demolding.

Packaging:

5 lb/pail, 20 lb/pail, 25 lb/pail, 30 lb/pail, 40 lb/pail, 50 lb/pail