Magnesium oxide, commonly known as magnesia, also referred to as magnesium oxide, is an alkaline oxide with the general properties of alkaline oxides and belongs to the category of cementitious materials. It is a white powder (with a pale yellow tint due to magnesium nitride), odorless, and is a typical alkaline earth metal oxide with the chemical formula MgO. The white powder has a melting point of 2852°C, a boiling point of 3600°C, and a relative density of 3.58 (at 25°C). It dissolves in acids and ammonium salt solutions but is insoluble in alcohol. Its solubility in water is 0.00062 g/100 mL (at 0°C).

0.0086 g/100 mL (30 °C). Exposed to air, it readily absorbs moisture and carbon dioxide, gradually becoming magnesia carbonate, with the light-weight variety undergoing the process faster than the heavy-weight. When combined with water under relative conditions, it forms magnesium hydroxide, exhibiting a slightly alkaline reaction with a pH of 10.3 in its saturated water solution. It dissolves in acids and ammonium salts but is poorly soluble in water, with its solution being alkaline. It is insoluble in ethanol. It has strong refractive properties in the visible and near-ultraviolet spectral range. Magnesium carbonate (MgCO3), dolomite (MgCO3·CaCO3), and seawater are the main raw materials for producing magnesium oxide. Magnesium oxide is obtained by thermal decomposition of magnesite or dolomite. Magnesium hydroxide precipitate is obtained by treating seawater with slaked lime, and magnesium oxide is obtained by calcining the magnesium hydroxide. Alternatively, magnesium chloride brine blocks obtained from the comprehensive utilization of seawater or brine obtained after bromine extraction can also be used as raw materials. By adding sodium hydroxide or sodium carbonate, magnesium hydroxide or basic magnesium carbonate precipitates are formed, which are then calcined to obtain magnesium oxide. China primarily uses magnesite, dolomite, brine, or brine blocks as raw materials [1].