310S (old grade 0Cr25Ni20/new grade 06Cr25Ni20) is an austenitic chromium-nickel stainless steel with excellent oxidation and corrosion resistance, due to its higher percentage of chromium and nickel. It boasts superior creep strength, allowing it to operate continuously at high temperatures with good high-temperature resistance.
Chemical Composition
C :≤0.08
Si :≤1.500
Mn :≤2.00
P :≤0.035
S :≤0.030
Ni :≤19.00-22.00
Cr :≤24.00-26.00
Mechanical properties
Tensile Strength (бb) (MPa): ≥520
Yield Strength (σs) (MPa): ≥205
Area Reduction (ψ)%: ≥50
Tensile strength (ób) ≥ 520 MPa, Yield strength (ó0.2) ≥ 205 MPa, Elongation at break (δ5) ≥ 40%, Shrinkage ratio (Ψ) ≥ 50%, Hardness (HB) ≤ 187. Withstanding high temperatures above 1150°C. Melting point ranges from 1398°C to 1454°C.