Chemical Formula: 2/3K2O·1/3Na22O·AI2O3·2SiO2·.9/2H2O
Silica-to-alumina ratio: SiO2/Al2O3≈2
Effective Aperture: Approximately 3A
Technical Specifications:
Indicator | Unit | Spherical | Rod | ||
Diameter | mm | 2-3 | 3-5 | 2-3 | 3-5 |
Static Water Absorption | ≥%wt | 21 | 20 | 20 | 20 |
Pile Density | ≥g/ml | 0.7 | 0.68 | 0.7 | 0.7 |
Compressive Strength | ≥N | 60 | 75 | 40 | 50 |
Wear rate | ≤%wt | 0.3 | 0.3 | 0.2 | 0.2 |
Loss on Ignition | ≤%wt | 1.5 | 1.5 | 1.5 | 1.5 |
Recycled:
1. Dehumidification: Depending on the pressure, temperature, and water content of the regasified air. Generally, dry gas at 200-350℃ is at 0.3-0.5 kg/cm.2Under pressure, pass through the molecular sieve bed for 3-4 hours to reach an outlet temperature of 110-180°C, then cool.
2. De-organic: Replace organic matter with steam, then remove moisture.。
Storage:
Room temperature, relative humidity not exceeding 90%; avoid direct exposure to air; prevent contact with water, acids, and alkalis.
Packaging: 25KG/piece. Specifics can be tailored to customer requirements.
Note:Avoid direct exposure of molecular sieve to air.