High-Temperature Glass Flake Mastic

Glass Flake Mortar (Medium Temperature)

Resin Type: Epoxy Acrylic Vinyl Ester Resin

Features: Excellent chemical resistance, solvent resistance, and impermeability

Main applications: lining for flue gas desulfurization units, various chemical equipment, etc.

Liquid: ≤120℃; Gas: ≤130℃; Appearance: White, semi-transparent, pale green, pale blue.

Achieve a coating thickness of 2mm in two to three coats.

Coating Methods: Blade and Trowel Application

Specific Gravity: 1.4-1.8

Coating Amount: Practical Value: 3.8 kg/m²

Construction Ratio (wt/%): Main Agent : Initiator : Accelerator

　　100：1～1.5：0.5～1

4 hours to 30 days interval

Operating conditions: Environmental temperature: 5℃-30℃

Relative Humidity: Below 85%

Packaging Agent: Iron Drum (20L)

Initiator and accelerator: plastic containers (5L or 10L)

Storage Method: Store in a cool, dry place, avoid direct sunlight.

Shelf life: 3 months at 20°C, 6 months at 15°C

Glass Flake Mortar (High Temperature)

Phenolic Epoxy Vinyl Ester Resin

Excellent chemical resistance, solvent resistance, and permeation resistance.

Primary applications include lining for flue gas desulfurization units, various chemical equipment, etc.

Liquid: ≤100℃; Gaseous: ≤200℃

Coating thickness: 2mm / completed in two to three coats

Coating Methods: Trowel and spatula application

Physical Appearance: White, semi-transparent/light green, light blue.

Specific Gravity: 1.4-1.8

Coating Amount: Practical Value: 3.5 kg/m²

Construction Ratio (wt/%): Main Agent : Initiator : Accelerator

　　100：1～1.5：0.5～1

Interval: 4 hours to 30 days

Operating conditions: environmental temperature: 5℃-30℃

Relative Humidity: Below 85%

Packaging Agent: Iron Drum (20L)

Initiator and Accelerator: Plastic Containers (5L or 10L)

Storage Method Store in a cool, dry place, avoid direct sunlight

Shelf life is three months at 20°C, six months at 15°C.

Product Description

1. Glass flake mortar features an anti-penetrating barrier with low permeability to corrosive gases.

2. Excellent resistance to water, acids, alkalis, some solvents, and other special chemical media.

3. Glass flake mortar has minimal shrinkage upon hardening, strong adhesion to various substrates, and is easy to repair locally.

4. High tensile glass flake mortar with excellent mechanical properties, adaptable to rapid temperature changes.

5. Glass flake adhesive mud cross-links and solidifies, featuring high surface hardness and excellent wear and corrosion resistance.

6. Long-term service temperature for glass flake mortar: wet state 100/180°C, dry state 120/200°C.

7. Compared to glass fiber reinforced plastic, the outstanding advantage of glass flake mortar is its excellent impermeability, with an impermeability rate approximately equal to that of glass fiber reinforced plastic.