Ceramic Particle Anti-Slip Road Surface
Bonding Strength (with Asphalt Concrete)
| ＞3 MPa (100% breaks within concrete)
| ACI-503 R29
|
Bonding Strength (with Concrete)
| > 5 MPa (breaks at 100% within concrete)
| ACI-503 R29
|
Shore D Hardness
| 40-50
| ASTM -2240
|
Compression Strength
| 47.6-54.4Mpa
| ASTM C-109
|
Tensile Strength (23℃)
| ＞17.2Mpa
| ASTM C-109
|
Tensile elongation (at 23°C)
| ＞35％
| ASTM C-109
|
Tensile Strength (0℃)
| ＞20Mpa
| ASTM C-109
|
Tensile elongation (at 0℃)
| ＞20％
| ASTM C-109
|
Tensile Strength (-10℃)
| ＞30Mpa
| ASTM C-109
|
Tensile elongation (-10℃)
| ＞10％
| ASTM C-109
|
Tensile Modulus
| 204-272Mpa
| ASTM C-109
|
Water Absorption Rate (Value)
| ＜0.1％
| ASTM C-243
|
Wear Resistance (Wear Test CS-17 wheel, 1000 cycles, 1000g)
| 60-70 mg
| ASTM C-501
|
Low-temperature bending creep, 7 days
| ＞0.165mm
| Test 419
|