XL-Z-22Waterborne epoxy intermediate coating
Waterborne epoxy intermediate coating is a two-component waterborne epoxy resin adhesive, a reactive curing type. It is an environmentally friendly material used for leveling epoxy flooring on concrete surfaces and mixed with quartz sand to prepare thick-coated epoxy patching mortar, which does not shrink or crack.
Use: For thick coating of waterborne epoxy flooring in construction, applicable to underground parking lots, schools, food factories, machinery factories, and power plants. It completely resolves issues such as odor during the construction of epoxy flooring and delamination caused by high moisture content in the base layer.
Features: Excellent coating leveling and cost-effectiveness; environmentally friendly, water-soluble, odorless, and non-toxic; can cure in moist conditions, with good breathability of the coating; high compressive strength and impact toughness; good wear resistance and heat shock resistance of the coating; quick drying, easy and fast application.
Technical Data:
Adhesion:1Grade
Compressive Strength:48MPa；
Rockwell Hardness:75；
Wear resistance:32mg；
Water resistance:120hNo issues.
User Guide:
Basic Requirement: The concrete strength of the basic ground must reachC25The surface must be smooth, dense, free of loose particles, oil stains, and other debris. There should be no condensation on the base surface, no standing water, and no specific moisture content requirements for the ground. However, it must meet the required strength (typically under normal ventilation conditions, new concrete)14The strength of the celestial queen).
Material Preparation: When in use, the temperature of the paint should be10Over 5°C, when the temperature is low, it is necessary to preheat the individual components first; otherwise, the paint viscosity is high, making it difficult to apply. When mixing, the components must be blended in the correct proportions.APour materials inBBlended in the material, using mechanical stirring, stirring time at least3Mix for minutes, until uniform in consistency. Stirring time may be appropriately extended based on the ambient temperature.
Usage Requirements:A、BAfter the material is well mixed, it is ready for use. It can also be used in appropriate quantities.0.1-03Mixed mm quartz sand, for use in preparing intermediate mortar.A、BAfter the material is mixed, it must60Exhausted within minutes.
Coating Method: Apply the pre-mixed middle coat mortar evenly using a trowel.
Coating Interval: After the coating surface is dry, it can be recoated. The waiting time will be extended when the temperature is low.
Construction Conditions: Environment and subgrade temperature must not be below5° C, not exceeding40°C, relative humidity of the air is less than85%。
Material Consumption:
Paints and quartz sand1：1Thick paste mortar mixed in proportion, typically applied in one coat for a single layer.1Coating thickness of approximately mm, paint consumption about0.2kg/㎡。
Packaging, Storage, and Transportation
19、Packaging, plastic drum packaging, assorted20、25、50Kilograms and other specifications
20、This product should be5-40°C Ventilated and dry storage room, storage period for12month
21、Non-hazardous goods, may be transported as general cargo.