main components

MC coating is a two-component self drying coating composed of epoxy modified silicone resin, pigments, additives, and solvents as component B, and a special epoxy curing agent as the other component.

Key Features

The paint film is hard; Excellent drying performance; High adhesion, good three proof performance, and excellent wear resistance.

main purpose

Widely used in various acidic, alkaline, and salt environments, it has excellent high temperature resistance and can withstand temperatures up to 250 ℃, while also requiring anti-corrosion equipment, containers, and flues.

technical indicators

Appearance of paint film: The paint film is flat and smooth, conforming to the standard board

Drying time: standard thickness single coating, 25 ℃, surface drying less than or greater than 2 hours, actual drying less than or greater than 24 hours Pencil hardness: greater than or equal to H

Adhesion: Theater equals 1 (circle drawing method, level)

Impact strength: 50kg/cm

Bending test: less than or equal to 1mm, heat resistance of 250 ℃, 6-hour loss of light greater than 30%, powdering less than or equal to level 3, water resistance of 30 days: no foaming

Acid resistance (10% sulfuric acid solution, 10 days): no wrinkling, no foaming, no shedding. Alkali resistance (10% sodium hydroxide solution, 10 days): no wrinkling, no foaming, no shedding