Molecular Formula:3/4CaO·1/4Na2O·AI2O3·2SiO2·.9/2H2O
Silica-to-alumina ratio:SiO2/AI2O3≈2
Effective Aperture:Approx. 5A
Technical Specifications:
Performance | Unit | Technical Specifications | |||
Shape | Thread | Ball | |||
Diameter | mm | 1.5-1.7 | 3.0-3.3 | 2.0-3.0 | 3.0-5.0 |
Particle size | % | ≥98 | ≥98 | ≥96 | ≥96 |
Stacking Density | G/ml | ≥0.65 | ≥0.65 | ≥0.70 | ≥0.70 |
Wear rate | % | ≤0.20 | ≤0.3 | ≤0.20 | ≤0.20 |
Compressive Strength | N | ≥23/cm | ≥18/cm | ≥50/p | ≥80/p |
Static Water Absorption | % | ≥20 | ≥20 | ≥21 | ≥21 |
n-hexane adsorption | % | ≥12 | ≥12 | ≥14 | ≥14 |
Water Content in Packaging | % | ≤1.5 | ≤1.5 | ≤1.5 | ≤1.5 |
Note:Above is commonly used5AMolecular sieve usage parameters may vary depending on different applications, with technical specifications adjusted accordingly. Please contact our company for specific technical data relevant to your application.
Recycled:1. Dewatering: Dependent on the pressure, temperature, and moisture content of the regasified air. Generally, dry gases at 200～350℃ are at a pressure of 0.3～0.5 kg/cm.2
Under pressure, pass through the molecular sieve bed for 3-4 hours to reach an outlet temperature of 110-180°C, then cool.
2. De-organic: Replace organic matter with steam, then remove moisture.
Storage:Room temperature, relative humidity not exceeding 90%; not suitable for direct exposure to air; avoid water, acids, and alkalis.
Packaging:Bottled or compound bag packaging. Specifics depend on customer requirements.
Note:Avoid direct exposure of the molecular sieve to the air.