CMC added to ceramic green bodies enhances their bonding strength, facilitates molding, increases bending strength, improves green body stability, and is particularly suitable for the machining of ceramic products. It boosts the processing speed of green bodies, reduces processing costs, and allows for even evaporation of moisture in the green body material, preventing cracking during drying and improving the yield of premium products.
Enhance the surface tension of the glaze
2. Ensures even dispersion of components within the glaze
3. Enhances the plasticity of silt materials, facilitating molding of the green body.
4. Enhance green body bending strength and glaze smoothness
Avoid flaking and the formation of bubbles due to strength changes in the body after glazing, and reduce pinholes in the glaze after drying to achieve a smooth and dense finish.
Primary Active Ingredient: Carboxymethyl Cellulose Grade: Ceramic Grade Brand: Nippon Chemical
Active Ingredient Content: 85% Product Specification: 25kg/bag Standard: GB1904-2005
Main Application: Ceramic Body Bottom Appearance: White Viscosity, mPa.s: 800
Replacement rate ≥ 0.7 pH value (10g/L water solution) 7.8 Dry loss, % ≤ 8.0
Chloride (C1 basis), % ≤ Heavy Metals (Pb basis), % ≤ Iron (Fe), % ≤