One: Main Ingredients:Aliphatic polyisocyanate

Section II: Product Description:The crosslinking agent can be dispersed directly with water and is mainly used for external crosslinking and curing of aqueous resin components, capable of crosslinking and curing at both room temperature and high temperatures.At 25°C, the adhesive has a usable time of up to 12 hours.

III. Performance Parameters:

Aesthetic: Transparent

Solids Content%）：100

Free-floatingHDI Monomer (%): ≤0.2

NCO（%）：18.5±0.5

Viscosity23℃，mPa.s）：4000±500

Color Value:≤60

Flarepoint℃）：>60

Densityg/ml）：1.08

Section 4: Application Scope:

Water-based printing paste and ink additives for external cross-linking, enhancing bonding properties and washfastness.

2. Water-based vacuum suction plastic curing agent, mix thoroughly and spray directly to enhance temperature resistance and prevent adhesive failure.

3. Waterborne polyurethane shoe adhesive curing agent.

4. Adding cross-linking agents to water-based wood coatings and paints enhances the film's luster, hardness, water resistance, solvent resistance, and weather resistance, among other properties.

How to Use:

1. Adhesive Application: This crosslinking agent exhibits excellent solubility in the aqueous phase, easily dispersing in various water-based coatings or adhesive systems. The recommended dosage is 3-10% of the non-volatile content in the water-based resin, and it is advised to use mechanical stirring to ensure uniform dispersion after addition.

2. Operation Precautions

1) Avoid long-term exposure to air after opening; seal with nitrogen before storage.

Operate in well-ventilated areas.

If contact with skin or eyes occurs, rinse thoroughly with plenty of water.

4) Any unused adhesive in the can should be disposed of promptly to prevent curing.

Six: StorageStore in a cool and dry environment; avoid temperatures exceeding30°C, shelf life of 12 months.

Packaging:1 Kg/iron can; 25 Kg/iron drum; 200 Kg/iron drum.