DW-6X 6Thick-walled heat shrinkable tubing
SexDistinctive features：
Product Description： |
Six times higher shrink ratio, with adhesive, high electricPressure-resistant, wear-resistant, sealed. Anti-Fashionable waterproof Product boasts excellent machinery.Mechanical properties, suitable for environments requiring environmental sealing and resistance to...Impact and wear resistance requirementsCable termination and intermediate connection protection.High compression ratio 6 Multiple sizes available for cables and connectors with varying dimensions. Head and electrical components |
SexCorrespond with key indicators： |
ReceivedShrinkage ratio:6 ：1 ContractionWarmDegree:120C Operating Temperature:-55 C~110C RingPacking Standard:RoHS Standard Color: Black |
Technical Specifications:
Test Items | Testing Method | Standard Value |
Operating Temperature | IEC 216 | -55C |
Tensile Strength | ASTM D 2671 | ≥ 14MPa |
Tensile elongation at break | ASTM D 2671 | ≥400% |
Tensile strength after aging(150C/168 Hour) | ASTM D 2671 | ≥ 12MPa |
elongation at break after aging(150C/168 Hour) | ASTM D 2671 | ≥300% |
Longitudinal shrinkage rate | UL 224 | 0 ~ 10% |
Penetration Strength | IEC 243 | ≥20kV/mm |
Volume resistivity | IEC 93 | ≥ 1014Q.cm |
Thermal shock(225C/4 Hour) | ASTM D 2671 | Crack-free, no dripping |
Hot Melt Adhesive
Absorption rate | ISO 62 | <0.2% |
Softening Point | ASTM D E28 | 85OC |
Peel Strength(PE) | DIN 30672 | 4 N/cm |
CopperStability | ASTM D 2671 | N/ACorrosion |
ISO 846
■ Product Specifications(Metric)：
Nominal Dimensions(mm) | Supply Should Measure Inch | Retracted dimensions(mm) | Tubular | Standard Length (mm) | ||
19/3.2 | 19.0 | 3.2 | 3.2 | O | 1000- 1200 | |
33/5.5 | 33.0 | 5.5 | 3.4 | O | 1000- 1200 | |
44.4/7.4 | 44.4 | 7.4 | 3.6 | O | 1000-1200 | |
50.8/8.3 | 50.8 | 8.3 | 4.3 | O | 1000- 1200 | |
69.8/11.7 | 69.8 | 11.7 | 4.8 | O | 1000- 1200 | |
88.9/17. 1 | 88.9 | 17.1 | 4.8 | O | 1000- 1200 | |
119.4/22.9 | 119.4 | 22.9 | 4.8 | O | 1000- 1200 | |
235/40 | 235 | 40 | 4.8 | O | 1000- 1200 | |
 | ||||||